Default Re: Bad manifold gaskets
Quote:
Originally Posted by dmaxweb View Post
What about rings cut from 316SS tube (1.500" OD X 16GA (0.065"))? With a significantly higher coefficient than cast iron can they still be solid or is a gap needed for thermal expansion?
Would it be better to use solid rings made from mild steel or cutting 304 stainless steel rings with a hacksaw to allow some thermal expansion?
dmaxweb is offline   Reply With Quote
 

« Previous Thread | Next Thread »

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump

Sponsored Links (Register now to hide all advertisements)


All times are GMT -5. The time now is 01:38 PM.