[ModelA29]

SS is not like regular steel that hardens if you quench it after heating.


Unlike martensitic steels, the austenitic stainless steels are not hardenable by heat treatment as no phase changes occur on heating or cooling. Softening is done by heating in the 1050/1200°C range, ideally followed by rapid cooling.