Re: I found a crack in an odd place while pressure testing
The problem with that particular area is that it is very thin. MIG cast iron, NO. I would find someone that is a proficient TIG welder. Pre heat and use nickel rod as a filler after drilling holes on each end of the crack. Stitching would work if the area was thicker.
|